Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Melt volume flow rate | | ISO 1133 | 100 cm3/10min |
| Shrinkage rate | | ISO 2577 | 1.1 - 1.3 % |
| Shrinkage rate | | ISO 2577 | 1.0 - 1.2 % |
| viscosity number | | ISO 307 | 145 cm³/g |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | FMVSS 302 | < 100 mm/min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1 | 4200 Mpa |
| tensile strength | | ISO 527-2/50 | 75.0 Mpa |
| Tensile strain | | ISO 527-2/50 | 14 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 45 kJ/m² |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 75 to 85 °C |
| drying time | | | 2.0 to 4.0 hr |
| Processing (melt) temperature | | | 240 to 280 °C |
| Temperature | | | 60 to 80 °C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | ISO 11357-3 | 221 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.