COC APEL™ APL5514ML MITSUI CHEM JAPAN
695
- Certificates:UL
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.04 | ||
| Shrinkage rate | ASTM D955 | 0.60% | % | |
| Melt mass flow rate | ASTM D1238/ISO 1133 | 36g/10min | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | ASTM D638/ISO 527 | 60 | kg/cm²(MPa)[Lb/in²] | |
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 25 | kg·cm/cm(J/M)ft·lb/in | |
| Bending modulus | ASTM D790/ISO 178 | 3200 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 100 | kg/cm²(MPa)[Lb/in²] | |
| Tensile elongation at break (elongation at break) | ASTM D638/ISO 527 | 3.0% | kg/cm²(MPa)[Lb/in²] | |
| Charpy impact strength | ASTM D256/ISO 179 | 10 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | ASTM D648/ISO 75 | 135 | ℃（℉） | |
| ASTM D648/ISO 75 | 125 | ℃（℉） |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Haze | ISO 14782 | 0.50% | % | |
| Light transmittance | ASTM D1003/ISO 13468 | 90% | % | |
| Refractive index | ASTM D542/ISO 489 | 1.540 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.