Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.81 g/cm³ |
| Apparent density | | ISO60 | 0.65 g/cm³ |
| Shrinkage rate | | ISO2577 | 0.10 % |
| Shrinkage rate | | ISO2577 | 0.050 % |
| Water absorption rate- | | ISO62 | 20.0 mg |
| PostShrinkage | | ISO2577 | 0.30 % |
| PostShrinkage | | ISO2577 | 0.25 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO2039-1 | 290 MPa |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| CompressionMoldingPressure | | | >15.0 MPa |
| CompressionMoldingTemperature | | | 160到190 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ISO527-2/5 | 60.0 MPa |
| Flexural modulus | | ISO178 | 13500 MPa |
| Bending stress | | ISO178 | 110 MPa |
| compression stress | | ISO604 | 250 MPa |
| Tensile modulus | | ISO527-2/1 | 12500 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179/1eU | 7.5 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | IEC60243-1 | 29 kV/mm |
| | IEC60250 | 7.50 |
| Dissipation Factor | | IEC60250 | 0.10 |
| CTI | | IEC60112 | 300 V |
| Surface Resistivity | | IEC60093 | 1E+11 ohms |
| Volume resistivity | | IEC60093 | 1E+12 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/C | 135 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.