PA6 POLIMID B B 10GF

Compare

Technical Data Sheet

other	Test Condition	Test Method	Test Result
notes			巴斯夫BASF B3EG2 其他相关资料.请联系波利尼龙总代理东莞轩阳塑胶原料有限公司
characteristic			10%碳纤增强PA6.机械强度高.电性能好.耐温高
Color			本色、黑色
purpose			适用于开关齿轮.摩托车零件.气柄.高尔夫球杆手柄.婴儿车轮零件.屠夫的钩子.剃须刀体等

processability	Test Condition	Test Method	Test Result
Dry conditions			90-100℃，≥3小时
Temperature			70-90 °C
Melt Temperature			230-260 °C

Mechanical properties	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ASTM D256/ISO 179	7.0 kg·cm/cm(J/M)ft·lb/in
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ASTM D256/ISO 179	35 kg·cm/cm(J/M)ft·lb/in
elongation at break		ASTM D638/ISO 527	120 %
Tensile modulus		ASTM D638/ISO 527	6000 kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	120 kg/cm²(MPa)[Lb/in²]
elongation		ASTM D638/ISO 527	6.0 %
elongation at break		ASTM D638/ISO 527	6.0 %

Physical properties	Test Method	Test Result
density	ASTM D792/ISO 1183	1.20
Shrinkage rate	ASTM D955	0.7-1.1 %
Water absorption rate	ASTM D570/ISO 62	1.1 %

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ASTM D648/ISO 75	210 ℃（℉）
Heat distortion temperature	Heat distortion temperature		ASTM D648/ISO 75	200 ℃（℉）
melting temperature			222 ℃（℉）
vicat		ASTM D1525/ISO R306	210 ℃（℉）

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.