HIPS

HIPS POLYREX® PH-88 BK TAIWAN CHIMEI

Properties:
High impact resistanceheat-resisting
Usages:
Lighting fixturesHousehold goodsElectronic fieldElectrical field
Compare View Prices

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	6.0 kJ/m²
	Impact strength of cantilever beam gap	23°C	ISO 180/1A	11 kJ/m²
		Impact strength of cantilever beam gap	23°C,6.40mm	ASTM D256	83 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	98 J/m
Charpy Notched Impact Strength	23°C	ISO 179	11 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179	6.5 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
bending strength	--6	ISO 178	37.0 Mpa
bending strength	bending strength	--5	ASTM D790	37.2 Mpa
Bending modulus	--6	ISO 178	2100 Mpa
Bending modulus	Bending modulus	--5	ASTM D790	1930 Mpa
elongation	Break	ISO 527-2/50	40 %
elongation	elongation	Break4	ASTM D638	40 %
tensile strength	Break	ISO 527-2/50	24.0 Mpa
	tensile strength	Break4	ASTM D638	23.5 Mpa
	tensile strength	tensile strength	Yield	ISO 527-2/50	26.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	MD	ISO 11359-2	4.0E-5到6.0E-5 cm/cm/°C
Vicat softening temperature	--	ISO 306/B50	90.0 °C
	Vicat softening temperature	--	ISO 306/A50	96.0 °C
	Vicat softening temperature	Vicat softening temperature	--	ASTM D15257	98.0 °C
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	80.0 °C
	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	74.0 °C
		Hot deformation temperature	1.8MPa,Annealed	ASTM D648	94.0 °C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	89.0 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate		ISO 294-4	0.40-0.70 %
Melt Volume Flow Rate (MVR)	200°C/5.0kg	ISO 1133	5.50 cm3/10min
melt mass-flow rate	200°C/5.0kg	ASTM D1238	6.0 g/10min
density	23°C	ISO 1183	1.03 g/cm³
density	density	--3	ASTM D792	1.05 g/cm³

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	L-Sale	ASTM D785	60

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

HIPS POLYREX® PH-88 BK TAIWAN CHIMEI

Technical Data Sheet