PC+ABS+SMA JCT1000 Americhem
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTM D995 | 0.40-0.60 % | |
| melt mass-flow rate | ASTM D1238 | 16.0 g/10min | |
| density | ASTM D792 | 1.19 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 122 R |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation at break | ASTM D638 | 4.0 % | |
| ASTM D638 | 90 % | ||
| bending strength | ASTM D790 | 95.1 MPa | |
| Flexural modulus | ASTM D790 | 2700 MPa | |
| Impact strength of cantilever beam gap | ASTM D256 | 641 J/m | |
| tensile strength | ASTM D638 | 60.0 MPa | |
| ASTM D638 | 55.8 MPa |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Nozzle opening size | 30-60 % | ||
| Mouth depth | 0.00381-0.00762 cm | ||
| screw speed | 30-75 rpm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 95.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.