| other | Test Condition | Test Method | Test Result |
|---|
| | | 低翘曲性、耐热性高、 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.42 g/cm |
| Water absorption rate | | ISO 62 | 0.2 % |
| Water absorption rate | | ISO 62 | 0.75 % |
| melt mass-flow rate | | ISO 1133 | 12.07 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| ball indentation hardness | | ISO 2039 part 1 | 140 Mpa |
| Yield tensile strength | | ISO 527 part 1/2 | 65 Mpa |
| elongation at break | | ISO 527 part 1/2 | 20 % |
| elongation | | ISO 527 part 1/2 | 9.0 % |
| Tensile modulus | | ISO 527 part 1/2 | 2800 Mpa |
| Flexural modulus | | ISO 178 | 2700 Mpa |
| Charpy without notch impact strength | | ISO 179 1eU | 12.0 J/cm |
| Charpy notch impact strength | | ISO 179 1eA | 0.6 J/cm |
| Charpy without notch impact strength | | ISO 179 1eU | 12 J/cm |
| Charpy notch impact strength | | ISO 179 1eA | 0.6 J/cm |
| Tensile creep modulus | | ISO 899 part 1 | 2400 Mpa |
| Tensile creep modulus | | ISO 899 part 1 | 1200 Mpa |
| Tensile modulus | | ASTM D638/ISO 527 | 566000 kg/cm²(MPa)[Lb/in²] |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | IEC 60250 | 4.20 |
| dielectric constant | | IEC 60250 | 4.20 |
| Dielectric Strength | | IEC 60243 part 1 | 35 KV/mm |
| Dissipation Factor | | IEC 60250 | 0.008 1 MHz |
| Dissipation Factor | | IEC 60250 | 0.0025 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 1.59 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO 11359 part 1/2 | 110 µm/m-℃ |
| melting point | | ISO 3146 method C1b | 166 °C |
| | ISO 75 part 1/2 | 100 °C |
| vicat | | ISO 306 | 150 °C |
| | ASTM D648/ISO 75 | 234 ℃（℉） |
| vicat | | ASTM D1525/ISO R306 | 304 ℃（℉） |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.