Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | 内部方法 | 1.43 g/cm³ |
| Shrinkage rate | | 内部方法 | 0.25 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | 内部方法 | 104 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | 内部方法 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Wear amount | | 内部方法 | 4.5 mg |
| tensile strength | | 内部方法 | 161 MPa |
| elongation | Break | 内部方法 | 1.8 % |
| Flexural modulus | | 内部方法 | 16900 MPa |
| bending strength | | 内部方法 | 243 MPa |
| coefficient of friction | | 内部方法 | 0.17 |
| Wear factor | | 内部方法 | 6 mm |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | 内部方法 | 12 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | 内部方法 | 263 °C |
| melting temperature | | 内部方法 | 281 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare