Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Apparent density | | ISO60 | 0.80 g/cm³ |
| Shrinkage rate | | ISO2577 | 0.35 % |
| Water absorption rate- | | ISO62 | 13.0 mg |
| PostShrinkage | | ISO2577 | 0.050 % |
| density | | ISO1183 | 1.85 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO2039-1 | 350 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| CompressionMoldingPressure | | | >15.0 MPa |
| CompressionMoldingTemperature | | | 160到190 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2/1 | 14000 MPa |
| Tensile stress | | ISO527-2/5 | 70.0 MPa |
| Flexural modulus | | ISO178 | 15500 MPa |
| Bending stress | | ISO178 | 130 MPa |
| compression stress | | ISO604 | 250 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 3.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 9.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Dissipation Factor | | IEC60250 | 0.020 |
| Volume resistivity | | IEC60093 | 1E+13 ohms·cm |
| dielectric strength | | IEC60243-1 | 24 kV/mm |
| | IEC60250 | 5.50 |
| Surface Resistivity | | IEC60093 | 1E+12 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/C | 115 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.