Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | g/cm³ | 1.35 -- |
| Shrinkage rate | | % | 0.60 -- |
| Shrinkage rate | | % | 0.10 -- |
| Water absorption rate | | % | 5.0 -- |
| Water absorption rate | | % | 2.0 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | MPa | 210 110 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | | HB -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Break | MPa | 190 125 |
| Tensile strain | Break | % | 3.0 8.0 |
| Tensile modulus | | MPa | 9700 6000 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | kJ/m² | 7.0 6.0 |
| Charpy Notched Impact Strength | | kJ/m² | 10 12 |
| Impact strength of simply supported beam without notch | | kJ/m² | 60 60 |
| Impact strength of simply supported beam without notch | | kJ/m² | 70 80 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ohms | -- 1E+12 |
| Volume resistivity | | ohms·cm | 1E+14 1E+13 |
| dielectric strength | | kV/mm | 25 21 |
| Compared to the Leakage Tracking Index (CTI) | | V | -- |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Continuous use temperature | | °C | 100to120 -- |
| Continuous use temperature | | °C | 230 -- |
| melting temperature | | °C | 260 -- |
| | cm/cm/°C | 2E-05 -- |
| Hot deformation temperature (HDT) | | °C | 235 -- |
| Hot deformation temperature (HDT) | | °C | 155 -- |
| | cm/cm/°C | 7E-05 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.