Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Resin | | 按重量计算的混合比:46按容量计算的混合比:4.0 |
| Hardener | | 按重量计算的混合比:34按容量计算的混合比:3.0 |
| | | 10到20 min |
| | | 26 wk |
| Thermosetting mixed viscosity | | ASTMD2393 | 750 cP |
| stripping time | | | 1400 min |
| stripping time | | | 60到120 min |
| stripping time | | | 30 min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ASTMD2240 | 7585 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Limiting Oxygen Index | | ASTMD2863 | 52 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | Yield | ASTMD638 | 1.0 % |
| elongation | Break | ASTMD638 | 2.2 % |
| Flexural modulus | | ASTMD790 | 7580 MPa |
| bending strength | Yield | ASTMD790 | 207 MPa |
| Tensile modulus | | ASTMD638 | 7580 MPa |
| tensile strength | Yield | ASTMD638 | 110 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 860 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTMD648 | 204 °C |
| | ASTMD696 | 2.2E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare