PA612 Zytel® 77G33L-BK031
244
- Properties:wear resistantHigh impact resistance
- Usages:Automotive ApplicationsFitness equipmentelectrical equipment
Compare
View PricesTechnical Data Sheet
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| PA612.33％玻纤增强.热稳定.注射成型 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 13 kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 12(-40℃) kg·cm/cm(J/M)ft·lb/in | ||
| elongation at break | ASTM D412/ISO 527 | 3 % | |
| Tensile modulus | ASTM D412/ISO 527 | 9500 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D412/ISO 527 | 168 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 8200 kg/cm²(MPa)[Lb/in²] |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.32 | |
| Shrinkage rate | ASTM D955 | 0.3-0.9 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| Hot deformation temperature (HDT) | ASTM D648/ISO 75 | 200 ℃（℉） | |
| melting temperature | 218 ℃（℉） | ||
| Linear expansion coefficient | ASTM D696/ISO 11359 | 0.83-1.58 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.