PI, TS APICAL 150AF019 Kaneka Corporation
0
- Usages:film
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D1505 | 1.53 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| film thickness | 38 µm | ||
| Secant modulus | ASTM D882 | 2790 MPa | |
| tensile strength | Break | ASTM D882 | 193 MPa |
| elongation | Break | ASTM D882 | 90 % |
| Elmendorf tear strength | ASTM D1922 | 18 g |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot wire ignition (HWI) | UL 746 | PLC 0 sec | |
| High arc combustion index (HAI) | UL 746 | PLC 3 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 4 mm/min | |
| Volume resistivity | ASTM D257 | 1E+15 ohms·cm | |
| dielectric strength | ASTM D149 | 180 kV/mm | |
| dielectric constant | ASTM D150 | 3.20 | |
| Dissipation Factor | ASTM D150 | 1.2E-03 | |
| arc resistance | ASTM D495 | 60.0 sec | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 3 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| RTI Elec | UL 746 | 240 °C | |
| RTI | UL 746 | 210 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.