POM N2200G53 BASF KOREA

Form：Granules | Grade：Enhanced level

Properties:

High hardnessGlass fiber reinforced

Typical Applications:

Automotive Applications

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive Applications
Properties:	High hardness \| Glass fiber reinforced

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	55	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	60	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
ISO Type		ISO 6383-1	POM-K. M-GNR. 02-003. GF25
Flammability level		UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile creep modulus	1000 hr	ISO 899-1	5800	Mpa
Tensile strain	Break	ISO 527-2	3.0	%
tensile strength	Break	ISO 527-2	130	Mpa
Tensile modulus		ISO 527-2	8800	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			100	°C
drying time			3.0	hr
Suggested maximum moisture content			0.20	%
Hopper temperature			200	°C
Temperature at the rear of the barrel			205	°C
Temperature in the middle of the barrel			205	°C
Temperature at the front of the material cylinder			210	°C
Spray nozzle temperature			210	°C
Processing (melt) temperature			190 to 230	°C
Mold temperature			60 to 120	°C
Residence Time			< 10.0	min
Screw speed			< 18	m/min
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Maximum operating temperature	短周期操作		110	°C
Linear coefficient of thermal expansion	23 to 55°C，Flow	ISO 11359-2	4.0E-5	cm/cm/°C
Melting temperature		ISO 11357-3	168	°C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	163	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	横向Flow	ISO 294-4	1.4	%
Melt Volume Flow Rate (MVR)	190°C/2.16 kg	ISO 1133	4.00	cm3/10min
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.15	%
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	0.90	%
Shrinkage rate	Flow	ISO 294-4	0.70	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index	Solution A	IEC 60112	PLC 0
Dissipation factor	1 MHz	IEC 60250	7.0E-3
Relative permittivity	1 MHz	IEC 60250	4.00
Dielectric strength		IEC 60243-1	85	KV/mm
Volume resistivity		IEC 60093	1.0E+14	ohms·cm
Surface resistivity		IEC 60093	1.0E+14	ohms
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test	H 961/30	ISO 2039-1	190	Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.