PPA UX08325 BK8115 SABIC INNOVATIVE NANSHA

Form：Granules | Grade：Injection grade

Properties:

Thermal stabilityCarbon fiber reinforcedFiller: Glass fiber reinf

Typical Applications:

Mechanical partsconsumer goods

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Mechanical parts \| consumer goods
Properties:	Thermal stability \| Carbon fiber reinforced \| Filler: Glass fiber reinf

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
23°C		ASTM D256	31	J/m
23°C	23°C		ISO 180/1A	2.9	kJ/m²
Suspended wall beam without notch impact strength	23°C	ASTM D4812	350	J/m
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
--1		ASTM D638	10900	Mpa
crack		ASTM D638	135	Mpa
	crack		ISO 527-2/5	125	Mpa
		crack		ASTM D638	1.9	%
		crack	crack		ISO 527-2/5	1.6	%
50.0mm span		ASTM D790	9770	Mpa
--5		ISO 178	9610	Mpa
--6		ISO 178	194	Mpa
Yield, 50.0mm span		ASTM D790	197	Mpa
Fracture, 50.0mm span		ASTM D790	195	Mpa
Fracture bending strain		ISO 178	2.1	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
1.8MPa, unannealed, 3.20mm		ASTM D648	264	°C
1.8MPa, unannealed, 64.0mm span of		ISO 75-2/Af	262	°C
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	2.2E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	5.4E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	MD	Internal Method	0.42	%
Shrinkage rate	Shrinkage rate	TD	Internal Method	0.53	%
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.54	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric constant	1.00GHz	ASTM D150	4.20
Dissipation factor	1.00GHz	ASTM D150	0.010

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.