HDPE+LLDPE Terralene® LL 1101 FKuR Kunststoff GmbH
0
- Usages:film
CompareTechnical Data Sheet
| 物理性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 密度 | ISO1183 | 0.921 g/cm³ | |
| 熔体质量流动速率 | 190°C/2.16kg | ISO1133 | 0.70到0.85 g/10min |
| 熔体体积流动速率 | 190°C/2.16kg | ISO1133 | 0.900到1.10 cm³/10min |
| 生物质含量-Carbon | ASTMD6866 | 90 % |
| 薄膜 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 薄膜厚度-经测试 | 20 µm | ||
| 拉伸模量 | MD:20µm | ISO527-3 | 290 MPa |
| ElmendorfTearStrength | TD:20.0µm | ISO6383-2 | 150.0 kN/m |
| SpencerImpact | 20.0µm | ASTMD3420 | 130.0 kN/m |
| 拉伸模量 | TD:20µm | ISO527-3 | 310 MPa |
| 拉伸应力 | MD:屈服,20µm | ISO527-3 | 37.0 MPa |
| TD:屈服,20µm | ISO527-3 | 32.0 MPa | |
| MD:断裂,20µm | ISO527-3 | 36.0 MPa | |
| TD:断裂,20µm | ISO527-3 | 31.0 MPa | |
| 伸长率 | MD:屈服,20µm | ISO527-3 | 680 % |
| TD:屈服,20µm | ISO527-3 | 690 % | |
| MD:断裂,20µm | ISO527-3 | 680 % | |
| TD:断裂,20µm | ISO527-3 | 690 % | |
| ElmendorfTearStrength | MD:20.0µm | ISO6383-2 | 50.0 kN/m |
| 机械性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 拉伸模量 | ISO527-2 | 330 MPa | |
| 拉伸应力 | Yield | ISO527-2 | 11.0 MPa |
| 拉伸应变 | Yield | ISO527-2 | 23 % |
| Break | ISO527-2 | >300 % |
| 热性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 熔融温度 | ISO3146 | 130到145 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.