| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.28 g/cm³ |
| Molten Volume Flow Rate (MVR) | | ISO 1133 | 42.0 cm3/10min |
| Shrinkage rate | | 内部方法 | 0.50 到 0.70 % |
| Shrinkage rate | | 内部方法 | 0.50 到 0.70 % |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | ISO 13468-1 | 0.6 % |
| Reflectivity 3 | | | 97.0 |
| ISO 9660 | | | >PC-MD10FR(40)< |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ISO 527-2 | 60.0 Mpa |
| Nominal tensile fracture strain | | ISO 527-2 | 60 % |
| Flexural modulus | | ISO 178 | 2600 Mpa |
| Bending stress | | ISO 178 | 90.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179 | 15 kJ/m² |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 120 °C |
| drying time | | | 5.0 到 8.0 hr |
| Temperature at the rear of the barrel | | | 260 到 280 °C |
| Temperature in the middle of the barrel | | | 260 到 280 °C |
| Temperature at the front of the material cylinder | | | 260 到 280 °C |
| Temperature | | | 80 到 90 °C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO 75-2/B | 127 °C |
| | ISO 75-2/A | 117 °C |
| | ISO 11359-2 | 6.5E-5 cm/cm/°C |
| RTI Elec | | UL 746 | 80.0 °C |
| RTI Imp | | UL 746 | 80.0 °C |
| RTI | | UL 746 | 80.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.