Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 0.70 g/10min |
| melt mass-flow rate | | ISO 1133 | 0.70 g/10min |
| Vinyl acetate content | | | 18.0 wt% |
| other | Test Condition | Test Method | Test Result |
|---|
| characteristic | | | 热稳定性 抗氧化性 |
| purpose | | | 工业领域 电线护套 |
| processability | Test Condition | Test Method | Test Result |
|---|
| Melt Temperature | | | <230 °C |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D-792 | 0.941 g/cm³ |
| melt mass-flow rate | | ASTM D-1238 | 0.7 g/10min |
| Vinyl acetate content | | | 18 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D-1708 | 63 Mpa |
| Shore hardness | | ASTM D-2240 | 92 |
| tensile strength | | ASTM D-1708 | 26 Mpa |
| elongation | | ASTM D-1708 | 600-900 % |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D1505 | 0.941 g/cm² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | ASTM D-3418 | 89 °C |
| vicat | | ASTM D-1525 | 68 °C |
| vicat | | ASTM E-28 | 223 °C |
| Haze ratio | | | 84 °C |
| vicat | | ASTM D1525 | 68.0 °C |
| vicat | | ISO 306 | 68.0 °C |
| melting temperature | | ASTM D3418 | 89.0 °C |
| melting temperature | | ISO 3146 | 89.0 °C |
| vicat | | ASTM D1525/ISO R306 | 68 ℃（℉） |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.