Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.33 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 110 R |
| Hardness (Shore) | | ASTM D2240 | 80 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | ASTM D-1003-61 | 87 ％ |
| Haze ratio | | ASTM D-1003-61 | 10 ％ |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 2210 MPa |
| tensile strength | | ASTM D638 | 41.4 MPa |
| bending strength | | ASTM D790 | 84.1 MPa |
| Flexural modulus | | ASTM D790 | 2550 MPa |
| Flexural modulus | | ASTM D-256 | 667 J/m |
| Flexural modulus | | ASTM D-1822 | 210 kJ/m² |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL -94 | V-0 1.00mm |
| UL flame retardant rating | | UL -94 | V-0 2.00mm |
| UL flame retardant rating | | UL -94 | V-0 3.00mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Hot deformation temperature (HDT) | | ASTM D648 | 62.2 °C |
| Hot deformation temperature (HDT) | | | 185 °C |
| Hot deformation temperature (HDT) | | ASTM D-696 | 6.84E-05 cm/cm／°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.