ABS H950 INEOS USA

127

Form：Granules | Grade：Heat resistant grade

Properties:

heat-resistingAging resistancewear resistantEasy to spray

Typical Applications:

Food service sectorAutomotive sectorApplication in the automotive fieldAutomotive External Parts

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Food service sector \| Automotive sector \| Application in the automotive field \| Automotive External Parts
Properties:	heat-resisting \| Aging resistance \| wear resistant \| Easy to spray

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179	140	kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/A	8.0	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179	90	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179	16	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179	7.0	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/A	17	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	80.0	Mpa
Bending modulus		ISO 178	2600	Mpa
Tensile strain	Yield,23°C	ISO 527-2	2.7	%
tensile strength	Yield,23°C	ISO 527-2	50.0	Mpa
Tensile modulus		ISO 527-2	2600	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	MD	ISO 11359-2	7E-05	cm/cm/°C
Vicat softening temperature		ISO 306/B50	113	°C
Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	101	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Annealed	ISO 75-2/B	108	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate		ISO 294-4	0.50-0.70	%
Melt Volume Flow Rate (MVR)	220°C/10.0kg	ISO 1133	4.00	cm3/10min
density		ISO 1183	1.05	g/cm³
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Relative permittivity	1MHz	IEC 60250	3.00
Relative permittivity	Relative permittivity	100Hz	IEC 60250	3.20
Dielectric strength	1.50mm	IEC 60243-1	37	KV/mm
Volume resistivity		IEC 60093	>1.0E+15	ohms·cm
Surface resistivity		IEC 60093	>1.0E+15	ohms
Dissipation factor	1MHz	IEC 60250	0.010
Dissipation factor	Dissipation factor	100Hz	IEC 60250	6E-03
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test		ISO 2039-1	110	Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.