PC/PBT 1760 SABIC INNOVATIVE JAPAN

Form：Granules | Grade：Injection grade

Properties:

Chemical resistanceHigh mobilityGlass fiber reinforcedHigh impact resistance

Typical Applications:

Automotive External Parts

Supplier(4)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive External Parts
Properties:	Chemical resistance \| High mobility \| Glass fiber reinforced \| High impact resistance

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	-30°C, Energy at Peak	ASTM D3763	3.00	J
	Dart impact	-30°C, Total Energy	ASTM D3763	3.00	J
		Dart impact	-20°C, Energy at Peak	ASTM D3763	4.00	J
		Dart impact	Dart impact	23°C, Total Energy	ASTM D3763	8.00	J
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	--1	ASTM D638	5310	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	4800	Mpa
tensile strength	Yield2	ASTM D638	84.0	Mpa
	tensile strength	Yield	ISO 527-2/5	84.0	Mpa
		tensile strength	Break2	ASTM D638	84.0	Mpa
		tensile strength	tensile strength	Break	ISO 527-2/5	84.0	Mpa
elongation	Yield2	ASTM D638	3.0	%
	elongation	Yield	ISO 527-2/5	3.0	%
		elongation	Break2	ASTM D638	3.0	%
		elongation	elongation	Break	ISO 527-2/5	3.0	%
Bending modulus	50.0 mm Span3	ASTM D790	3910	Mpa
Bending modulus	Bending modulus	--4	ISO 178	4010	Mpa
bending strength	--4,5	ISO 178	133	Mpa
bending strength	bending strength	Yield, 50.0 mm Span3	ASTM D790	131	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			110	°C
drying time			4.0 to 6.0	hr
Suggested maximum moisture content			0.020	%
Suggested injection volume			50 to 80	%
Temperature at the rear of the barrel			250 to 270	°C
Exhaust hole depth			0.013 to 0.020	mm
Screw speed			50 to 80	rpm
Back pressure			0.300 to 0.600	Mpa
Mold temperature			65 to 95	°C
Processing (melt) temperature			260 to 280	°C
Spray nozzle temperature			255 to 275	°C
Temperature at the front of the material cylinder			260 to 280	°C
Temperature in the middle of the barrel			255 to 275	°C
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	125	°C
	Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	116	°C
	Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span7	ISO 75-2/Af	101	°C
Vicat softening temperature	--	ASTM D15258	121	°C
	Vicat softening temperature	--	ISO 306/B50	135	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	130	°C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	3.9E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	7.6E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	7.6E-5	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	250°C/5.0 kg	ASTM D1238	15	g/10 min
Melt Volume Flow Rate (MVR)	265°C/5.0 kg	ISO 1133	27.0	cm3/10min
Shrinkage rate	Flow : 3.20 mm	Internal Method	0.40 - 0.60	%
Shrinkage rate	Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.40 - 0.60	%
Water absorption rate	Saturation, 23°C	ISO 62	0.50	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.15	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PC/PBT 1760 SABIC INNOVATIVE JAPAN

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index