Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ASTM D570 | 0.10 % |
| density | | ASTM D792 | 1.74 g/cm³ |
| Shrinkage rate | | ASTM D1895 | 2.0 |
| Shrinkage rate | | ASTM D955 | 0.10to0.20 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 100 |
| Rockwell hardness | M-Scale | ASTM D785 | 120 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ASTM D790 | 16500 MPa |
| bending strength | Yield | ASTM D790 | 165 MPa |
| compressive strength | | ASTM D695 | 276 MPa |
| tensile strength | Yield | ASTM D638 | 64.8 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 48 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTM D149 | 15 kV/mm |
| arc resistance | | ASTM D495 | 180 sec |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 271 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 3.8E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.