Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.04 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 1.6 g/10min |
| density | | ISO 1183 | 1.05 g/cm³ |
| Shrinkage rate | | ISO 294-4 | 0.40to0.70 % |
| Melt volume flow rate | | ISO 1133 | 19.0 cm³/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 113 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179 | 25 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179 | 12 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 24 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 11 kJ/m² |
| Impact strength of cantilever beam gap | | ASTM D256 | 250 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 280 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ISO 178 | 71.0 MPa |
| bending strength | | ASTM D790 | 71.0 MPa |
| Flexural modulus | | ISO 178 | 2000 MPa |
| Flexural modulus | | ASTM D790 | 1720 MPa |
| elongation | Break | ISO 527-2/50 | 25 % |
| tensile strength | | ASTM D638 | 45.4 MPa |
| tensile strength | Yield | ISO 527-2/50 | 46.0 MPa |
| tensile strength | Break | ISO 527-2/50 | 34.0 MPa |
| elongation | | ASTM D638 | 40 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | ISO 11359-2 | 8.8E-05 cm/cm/°C |
| vicat | | ISO 306/B50 | 98.0 °C |
| vicat | | ISO 306/A50 | 105 °C |
| vicat | | ASTM D15257 | 106 °C |
| Heat distortion temperature | | ISO 75-2/A | 100 °C |
| Heat distortion temperature | | ASTM D648 | 97.0 °C |
| Heat distortion temperature | | ISO 75-2/A | 83.0 °C |
| Heat distortion temperature | | ASTM D648 | 87.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.