physical property | Test Condition | Test Method | Test Result |
---|
density | | ISO 1183 | 0.938 g/cm³ |
melt mass-flow rate | | ISO 1133 | 1.7 g/10min |
density | | ISO 1183 | 0.938 g/cm³ |
melt mass-flow rate | | ISO 1133 | 1.7 g/10min |
hardness | Test Condition | Test Method | Test Result |
---|
Shore hardness | | ISO 868 | 50 |
Shore hardness | | ISO 868 | 50 |
elastomer | Test Condition | Test Method | Test Result |
---|
compression set | | ISO 815 | 39 % |
tensile strength | | ISO 37 | 1.20 MPa |
tensile strength | Yield | ISO 37 | 14.0 MPa |
elongation | Break | ISO 37 | 960 % |
tear strength | | ISO 34-1 | 35 kN/m |
compression set | | ISO 815 | 39 % |
compression set | | ISO 815 | 34 % |
compression set | | ISO 815 | 34 % |
tensile strength | | ISO 37 | 1.20 MPa |
tensile strength | Yield | ISO 37 | 14.0 MPa |
elongation | Break | ISO 37 | 960 % |
tear strength | | ISO 34-1 | 35 kN/m |
aging | Test Condition | Test Method | Test Result |
---|
Change rate of tensile strength in air | | ISO 1817 | -4.0 % |
Change rate of tensile strength in air | | ISO 1817 | -4.0 % |
Tensile stress change rate | | ISO 1817 | 13 % |
Tensile stress change rate | | ISO 1817 | 13 % |
Thermal performance | Test Condition | Test Method | Test Result |
---|
brittle temperature | | ISO 974 | -60.0 °C |
brittle temperature | | ISO 974 | -60.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.