PP Polifor® ECO 30 CA/40 GRIGIO Y1 SO.F.TER ITALY

Properties:
Filler mineral filler 40% filler by weight
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ASTM D256	23 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D256	23 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	3.2mm	UL 94	HB
	UL flame retardant rating	1.6mm	UL 94	HB
		UL flame retardant rating	3.2mm	UL 94	HB
		UL flame retardant rating	UL flame retardant rating	1.6mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus		ASTM D790	1900 MPa
Bending modulus	Bending modulus		ASTM D790	1900 MPa
elongation	Break	ASTM D638	30 %
tensile strength	Yield	ASTM D638	20.0 MPa
elongation	Break	ASTM D638	30 %
tensile strength	Yield	ASTM D638	20.0 MPa

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature		ASTM D15252	93.0 °C
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	57.0 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	57.0 °C
Vicat softening temperature		ASTM D15252	93.0 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate		Internal Method	1.3 %
melt mass-flow rate	230°C/2.16kg	ASTM D1238	19 g/10min
density		ASTM D792	1.24 g/cm³
Shrinkage rate		Internal Method	1.3 %
melt mass-flow rate	230°C/2.16kg	ASTM D1238	19 g/10min
density		ASTM D792	1.24 g/cm³

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.