PA6 B50H1 SOLVAY SHANGHAI

Form：Granules | Grade：Flame retardant grade

Properties:

High rigidityThermal stability

Typical Applications:

Laptop caseElectronic fieldElectrical fieldPipe fittingscurrencypipelineProfile

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Laptop case \| Electronic field \| Electrical field \| Pipe fittings \| currency \| pipeline \| Profile
Properties:	High rigidity \| Thermal stability

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	80	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	70	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.40mm	UL 94	V-0
	UL flame retardant rating	0.8mm	UL 94	V-0
		UL flame retardant rating	1.6mm	UL 94	V-0
		UL flame retardant rating	UL flame retardant rating	3.2mm	UL 94	V-0
Burning wire flammability index	0.8mm	IEC 60695-2-12	960	°C
	Burning wire flammability index	1.6mm	IEC 60695-2-12	960	°C
	Burning wire flammability index	Burning wire flammability index	3.2mm	IEC 60695-2-12	960	°C
Ignition temperature of heating wire	1.6mm	IEC 60695-2-13	650	°C
Extreme Oxygen Index		ISO 4589-2	33	%
UL flame retardant rating		NFF16-101	F2
smoke density		NFF16-101	I2
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	23°C	ISO 527-2/1A	3750	Mpa
tensile strength	Yield,23°C	ASTM D638	85.0	Mpa
	tensile strength	Yield,23°C	ISO 527-2/1A	80.0	Mpa
	tensile strength	tensile strength	Break,23°C	ISO 527-2/1A	70.0	Mpa
Tensile strain	Yield,23°C	ISO 527-2	4.0	%
elongation	Break,23°C	ASTM D638	15	%
Tensile strain	Break,23°C	ISO 527-2	12	%
Bending modulus	23°C	ASTM D790	3800	Mpa
Bending modulus	Bending modulus	23°C	ISO 178	3700	Mpa
bending strength	23°C	ASTM D790	125	Mpa
bending strength	bending strength	23°C	ISO 178	130	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	85.0	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/Af	85.0	°C
Melting temperature		ISO 11357-3	242	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	23°C,24hr	ISO 62	1.1	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	3.1	%
Outdoor applicability		UL 746C	f1
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 0
Surface resistivity		IEC 60093	1E+15	ohms
Volume resistivity		IEC 60093	1E+15	ohms·cm
Dielectric strength	0.800mm	IEC 60243-1	33	KV/mm
Relative permittivity		IEC 60250	3.60
Dissipation factor		IEC 60250	0.020
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
EuropeanRailwaysCertifications	R22	EN45545-2	HL2
EuropeanRailwaysCertifications	EuropeanRailwaysCertifications	R23	EN45545-2	HL3

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.