Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Apparent density | | ASTM D1895 | 0.65 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 3.5 g/10min |
| density | | ASTM D792 | 1.04 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 72 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 2300 MPa |
| tensile strength | | ASTM D638 | 24.0 MPa |
| tensile strength | | ASTM D638 | 26.0 MPa |
| elongation | | ASTM D638 | 65 % |
| Flexural modulus | | ASTM D790 | 2100 MPa |
| bending strength | | ASTM D790 | 43.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 150 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 89.0 °C |
| vicat | | ASTM D15253 | 102 °C |
| vicat | | ASTM D15254 | 95.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare