PA12 Generic Nylon 12 - Glass Fiber

Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density		ASTM D792	1.15to1.38 g/cm³
density	density		ISO 1183	1.11to1.70 g/cm³
Shrinkage rate		ASTM D955	0.10to0.41 %
Shrinkage rate	Shrinkage rate		ISO 294-4	0.10to0.71 %
Water absorption rate		ASTM D570	0.091to0.60 %
	Water absorption rate		ISO 62	0.10to0.41 %
		Water absorption rate		ASTM D570	0.40to1.2 %
			Water absorption rate		ISO 62	0.80to1.2 %
			Water absorption rate	Water absorption rate		ISO 62	0.39to0.60 %

Impact resistance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength		ASTM D256	570to1400 J/m
Charpy Notched Impact Strength		ISO 179	10to26 kJ/m²
Impact strength of simply supported beam without notch		ISO 179	47to100 kJ/m²
Impact strength of cantilever beam gap		ASTM D256	85to260 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO 180	1.8to18 kJ/m²

Mechanical properties	Test Condition	Test Method	Test Result
tensile strength		ISO 527-2	99.1to130 MPa
	tensile strength		ASTM D638	106to151 MPa
		tensile strength		ISO 527-2	63.8to191 MPa
		tensile strength	tensile strength		ASTM D638	92.9to108 MPa
elongation		ASTM D638	1.8to10 %
	elongation		ISO 527-2	1.5to7.0 %
		elongation		ASTM D638	1.8to11 %
		elongation	elongation		ISO 527-2	1.5to7.6 %
Flexural modulus		ASTM D790	3720to9050 MPa
tensile strength		ASTM D638	85.4to130 MPa
Tensile modulus		ASTM D638	5880to16100 MPa
Tensile modulus	Tensile modulus		ISO 527-2	3910to19200 MPa
Flexural modulus		ISO 178	11.0to9000 MPa
bending strength		ASTM D790	93.6to244 MPa
bending strength	bending strength		ISO 178	96.0to213 MPa

Electrical performance	Test Method	Test Result
dielectric strength	IEC 60243-1	18to44 kV/mm
relative permittivity	IEC 60250	3.75
Compared to the Leakage Tracking Index (CTI)	IEC 60112	PLC 0
Volume resistivity	IEC 60093	1.0E+2到1.0E+15 ohms·cm

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ASTM D648	160to174 °C
	Heat distortion temperature		ISO 75-2/A	150to176 °C
	Heat distortion temperature	Heat distortion temperature		ISO 75-2/C	80.0to160 °C
Continuous use temperature		ASTM D794	104to151 °C
vicat		ISO 306	170to175 °C
Heat distortion temperature		ASTM D648	176to178 °C
Heat distortion temperature	Heat distortion temperature		ISO 75-2/B	169to178 °C
melting temperature			174to185 °C
melting temperature	melting temperature		ISO 11357-3	178 °C
Linear coefficient of thermal expansion		ASTM D696	8.0E-6到4.9E-5 cm/cm/°C
	Linear coefficient of thermal expansion		ISO 11359-2	1.0E-5到4.2E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion		ISO 11359-2	6.9E-5到1.5E-4 cm/cm/°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.