PA6 B2S35 V2-7035
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.16 g/cm³ | |
| ISO 1183/A | 1.16 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-2 | |
| UL 94 | V-2 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | ISO 178 | 80.0 MPa | |
| Tensile modulus | ISO 527-2/1 | 3300 MPa | |
| tensile strength | Break | ISO 527-2/5 | 75.0 MPa |
| Tensile strain | Yield | ISO 527-2/5 | 4.0 % |
| Flexural modulus | ISO 178 | 1800 MPa | |
| bending strength | ISO 178 | 80.0 MPa | |
| Charpy Notched Impact Strength | ISO 179/1eA | 3.0 kJ/m² | |
| ISO 179/1eU | 无断裂 | ||
| Tensile strain | Yield | ISO 527-2 | 4.0 % |
| Flexural modulus | ISO 178 | 1800 MPa | |
| Tensile modulus | ISO 527-2 | 3300 MPa | |
| tensile strength | Break | ISO 527-2 | 75.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 3.0 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179/1eU | 无断裂 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature (HDT) | ISO 75-2/A | 55.0 °C | |
| vicat | ISO 306/B | 200 °C | |
| Hot deformation temperature (HDT) | ISO 75-2/A | 55.0 °C | |
| vicat | ISO 306 | 200 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.