POM C9021S CELANESE GERMANY

Form：Granules | Grade：Injection grade

Properties:

wear resistantcurrency

Typical Applications:

Household appliancesHousehold appliancesAutomotive sectorFitness equipmentThin walled products

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Household appliances \| Household appliances \| Automotive sector \| Fitness equipment \| Thin walled products
Properties:	wear resistant \| currency

Certificates

No Data...

Technical Data Sheet

Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	8.5cm	ISO 1133	12.07	g/10min
Water absorption rate	Saturation23℃	ISO 62	0.75	%
Water absorption rate	Water absorption rate	23℃and50%RH	ISO 62	0.2	%
density		ISO 1183	1.42
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile creep modulus	1000 hours	ISO 899 part 1	1200	Mpa
Tensile creep modulus	Tensile creep modulus	1 hour	ISO 899 part 1	2400	Mpa
Charpy Notched Impact Strength	23℃	ISO 179 1eA	0.6	J/cm
elongation	伸长率	ISO 527 part 1/2	9.0	%
Elongation at Break	50mm/min	ISO 527 part 1/2	20	%
tensile strength	50mm/min，Yield	ISO 527 part 1/2	65	Mpa
Ball Pressure Test	30sec数值	ISO 2039 part 1	140	Mpa
Impact strength of simply supported beam without notch	低温-30℃	ISO 179 1eU	12	J/cm
Charpy Notched Impact Strength	低温-30℃	ISO 179 1eA	0.6	J/cm
Impact strength of simply supported beam without notch	23℃	ISO 179 1eU	12.0	J/cm
Bending modulus		ISO 178	2700	Mpa
Tensile modulus	1mm/min	ISO 527 part 1/2	2800	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature	VST/B/50	ISO 306	150	°C
Hot deformation temperature	1.8MPa	ISO 75 part 1/2	100	°C
Melting temperature	DSC,10 K/min	ISO 3146 method C1b	166	°C
Linear coefficient of thermal expansion	23-55℃ Longitudinal	ISO 11359 part 1/2	110	µm/m-℃
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric strength		IEC 60243 part 1	35	KV/mm
Dielectric constant	低频100 Hz	IEC 60250	4.20
Dielectric constant	Dielectric constant	1 MHz	IEC 60250	4.20
Dissipation factor	低频100 Hz	IEC 60250	0.0025
Dissipation factor	Dissipation factor		IEC 60250	0.008	1 MHz

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.