Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D955 | 0.40 % |
| Shrinkage rate | | ASTM D955 | 0.80 % |
| Water absorption rate | | ASTM D570 | 0.23 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 12000 Mpa |
| tensile strength | | ISO 527-2 | 210 Mpa |
| Tensile strain | | ISO 527-2 | 2.5 % |
| Flexural modulus | | ISO 178 | 10700 Mpa |
| bending strength | | ISO 178 | 295 Mpa |
| Bending Strain | | ISO 178 | 3.1 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 79 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180/1U | 68 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Dissipation Factor | | ASTM D150 | 0.015 |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 0 |
| High Voltage Arc Traceability Rate (HVTR) | | UL 746 | mm/min |
| Volume resistivity | | ASTM D257 | 5.6E+15 ohms·cm |
| dielectric strength | | ASTM D149 | 19 KV/mm |
| dielectric constant | | ASTM D150 | 4.10 |
| dielectric constant | | ASTM D150 | 3.75 |
| Dissipation Factor | | ASTM D150 | 6E-03 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | ISO 11357-3 | 327 °C |
| Linear coefficient of thermal expansion | | ASTME831 | 2E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTME831 | 1.5E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTME831 | 7.6E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTME831 | 1.2E-04 cm/cm/°C |
| Heat distortion temperature | | ISO 75-2/A | >300 °C |
| Glass Transition Temperature | | DSC | 95.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.