Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | GB/T2914 | 0.02 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | GB/T 1040 | 130 Mpa |
| elongation at break | | GB/T 1040 | 1.3 % |
| bending strength | | GB/T 9341 | 200 Mpa |
| Flexural modulus | | GB/T 9341 | 1.1×10000 Mpa |
| Impact strength of cantilever beam gap | | GB/T 1843 | 11 kJ/m² |
| coefficient of friction | | GB/T3960 | 0.3 V |
| Other performance | Test Condition | Test Method | Test Result |
|---|
| Wear scar width | | GB/T3960 | 4.5 mm |
| Wear amount | | GB/T3960 | 3.5 mg/120min |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | GB/T 1033 | 1.61 g/cm³ |
| Mold Shrinkage | | GB/T15585 | 0.25/0.60 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | GB/T1410 | 5 ×1015 Q.m |
| Surface Resistivity | | GB/T1410 | 5 ×1014 Q |
| electric strength | | GB/T 1408 | 16 KV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting point | | GB/T4608 | 280 ℃ |
| Hot deformation temperature (1.8MPa) | | GB/T1634 | 262 ℃ |
| Flame retardancy | | GB/TUL94 | V-0 V |
| unknown | Test Condition | Test Method | Test Result |
|---|
| Valence constant 1MHz | | GB/T 1409 | 4 V |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.