PP 3210G6 ENC1 NAN YA TAIWAN

Form：Granules

Properties:

Low contractilityheat-resistinghigh strengthGlass fiber reinforcedHigh rigidity20% mineral fiber reinfor30% glass fiber reinforceHigh rigidityLow shrinkageHigh mechanical strengthHeat resistance

Typical Applications:

Shellsmall home appliancesHousehold appliancesBobbinPump casingController housingHome appliance products etc

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Shell \| small home appliances \| Household appliances \| Bobbin \| Pump casing \| Controller housing \| Home appliance products \| etc
Properties:	Low contractility \| heat-resisting \| high strength \| Glass fiber reinforced \| High rigidity \| 20% mineral fiber reinfor \| 30% glass fiber reinforce \| High rigidity \| Low shrinkage \| High mechanical strength \| Heat resistance

Certificates

No Data...

Technical Data Sheet

Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate		ASTM D-1238	3.0	g/10min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength		ASTM D638	32	Mpa
tensile strength	tensile strength	Yield	ASTM D-638	870	kg/cm2
Impact strength of cantilever beam gap		ASTM D-256	9	kg.cm/cm
Bending modulus		ASTM D-790	45000	kg/cm2
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Melting temperature		DSC法	165	°C
Hot deformation temperature	HDT	ASTM D-648	160	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate		ASTM	0.3-0.7	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		ASTM D257	10^16	Ω.cm
Dielectric strength		ASTM D-149	40	KV/mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.