PA/ABS N NM-11 BASF USA

Form：Granules | Grade：Injection grade

Properties:

High mobilityHigh impact resistanceEasy to process

Typical Applications:

Helmetsporting goodsAutomotive sectorShellApplication in the automotive field

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Helmet \| sporting goods \| Automotive sector \| Shell \| Application in the automotive field
Properties:	High mobility \| High impact resistance \| Easy to process

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179	无断裂
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile strain	Yield,23°C	ISO 527-2	3.5	%
Bending modulus		ISO 178	1800	Mpa
bending strength		ISO 178	62.0	Mpa
Tensile modulus		ISO 527-2	2000	Mpa
tensile strength	Yield,23°C	ISO 527-2	43.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Annealed	ISO 75-2/B	85.0	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	65.0	°C
Vicat softening temperature	--	ISO 306/A50	160	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	102	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	1E-04	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Melt Volume Flow Rate (MVR)	240°C/10.0kg	ISO 1133	30.0	cm3/10min
Shrinkage rate		ISO 294-4	0.80	%
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.2	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	1E+14	ohms
Volume resistivity		IEC 60093	>1.0E+15	ohms·cm
Relative permittivity	1MHz	IEC 60250	2.90
Dissipation factor	1MHz	IEC 60250	0.015
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test		ISO 2039-1	86.0	Mpa
film	Test Condition	Test Method	Test Result	Test Unit
elongation	Break	ISO 527-3	>50	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.