ABS

ABS Nilac 010 Soredi S.p.a.

Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	200 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-20°C,3.20mm	ASTM D256	100 J/m

flammability	Test Condition	Test Method	Test Result
Hot filament ignition temperature		IEC 60695-2-13	650 °C
UL flame retardant rating	3.2mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	1.6mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Break	ASTM D790	65.0 MPa
Bending modulus		ASTM D790	2400 MPa
elongation	Break	ASTM D638	30 %
tensile strength	Yield	ASTM D638	44.0 MPa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	9E-05 cm/cm/°C
Vicat softening temperature		ASTM D15254	98.0 °C
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	92.0 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.30 %
Shrinkage rate	MD	ASTM D955	0.40to0.70 %
melt mass-flow rate	220°C/10.0kg	ASTM D1238	24 g/10min
density		ASTM D792	1.05 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Dissipation factor	1MHz	IEC 60250	0.010
Relative permittivity	1MHz	IEC 60250	2.80
Dielectric strength	1.00mm	IEC 60243-1	30 kV/mm
Volume resistivity		IEC 60093	1E+15 ohms·cm
Surface resistivity		IEC 60093	1E+15 ohms

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	110

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.