PA6 BKV30GH2.0 900116 LANXESS GERMANY

Form：Granules | Grade：Injection grade

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	60	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	55	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	65	kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	55	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
BurningBehavior		ISO 3795	passed
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	23°C	ASTM D638	8730	Mpa
Tensile modulus	Tensile modulus	23°C	ISO 527-2/1	9400	Mpa
tensile strength	Break,23°C	ASTM D638	165	Mpa
tensile strength	tensile strength	Break,23°C	ISO 527-2/5	170	Mpa
elongation	Break,23°C	ASTM D638	3.2	%
Tensile strain	Break,23°C	ISO 527-2/5	3.0	%
Bending modulus	23°C	ASTM D790	8000	Mpa
Bending modulus	Bending modulus	23°C	ISO 178/A	8400	Mpa
bending strength	23°C	ASTM D790	260	Mpa
	bending strength	3.5%Strain	ISO 178/A	255	Mpa
		bending strength	23°C	ISO 178	260	Mpa
		bending strength	bending strength	FlexuralStrainatFlexuralStrength5(23°C)		3.6	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	219	°C
	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	210	°C
	Hot deformation temperature	Hot deformation temperature	8.0MPa,Unannealed	ISO 75-2/C	150	°C
Vicat softening temperature		ISO 306/B120	210	°C
Ball Pressure Test	210°C	IEC 60695-10-2	Pass
Melting temperature		ISO 11357-3	221	°C
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	2E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	1E-04	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Apparent density		ISO 60	0.60	g/cm³
Shrinkage rate	TD:280°C,2.00mm2	ISO 294-4	0.81	%
	Shrinkage rate	TD:120°C,2hr,2.00mm3	ISO 294-4	0.10	%
		Shrinkage rate	MD:280°C,2.00mm2	ISO 294-4	0.29	%
		Shrinkage rate	Shrinkage rate	MD:120°C,2hr,2.00mm3	ISO 294-4	0.050	%
Water absorption rate	Saturation,23°C	ISO 62	7.0	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	2.1	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric strength	23°C,1.00mm	IEC 60243-1	33	KV/mm
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 1
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test		ISO 2039-1	193	Mpa
film	Test Condition	Test Method	Test Result	Test Unit
Thin film puncture strength	--6	ISO 6603-2	2.10	J
	Thin film puncture strength	--7	ISO 6603-2	2.20	J
		Thin film puncture strength	--6	ISO 6603-2	744	N
		Thin film puncture strength	Thin film puncture strength	--7	ISO 6603-2	803	N
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
ISO Shortcut		ISO 1874	PA6.GHR.10-090.GF30

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.