Technical Data Sheet
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| DemoldTime | | | 1.0 hr |
| DemoldTime | | | 7.0到8.0 min |
| DemoldTime | | | 6.0到7.0 min |
| DemoldTime | | | 5.0-6.0 hr |
| | | 按重量计算的混合比:100 |
| | | 按重量计算的混合比:50 |
| Shelf Life | | 26 wk |
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.22 g/cm³ |
| density | | | 1.157 g/cm³ |
| density | | | 1.157 g/cm³ |
| density | | | 0.80 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ASTMD2240 | 82到86 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| CureTime | | | 16.0到24.0 hr |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| Brookfield viscosity | | | 850 mPa·s |
| Brookfield viscosity | | | 1000 mPa·s |
| Brookfield viscosity | | | 650 mPa·s |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | Yield | ASTMD638 | 9.1 % |
| Flexural modulus | | ASTMD790 | 2190 MPa |
| bending strength | | ASTMD790 | 87.6 MPa |
| Tensile modulus | | ASTMD638 | 2020 MPa |
| tensile strength | Yield | ASTMD638 | 71.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 47 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 171 °C |
| | ASTMD648 | 103 °C |
| | ASTME831 | 1.3E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.