Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.19 g/cm³ |
| Water absorption rate | | ASTM D570 | 0.35 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 90to100 |
| Barcol Hardness | | ASTM D2583 | 48to52 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | ASTM D1003 | 93.0 % |
| Haze ratio | | ASTM D1003 | 0.80 % |
| Haze ratio | | ASTM D1003 | <2.0 % |
| Yellowness Index | | ASTM D1925 | 0.50 YI |
| UV Transmittance | | | <1.0 % |
| refractive index | | ASTM D542 | 1.490 |
| transmissivity | | ASTM D1003 | 93.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| HotFormingTemperature | | 内部方法 | 160to193 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 68.9 MPa |
| elongation | | ASTM D638 | 5.0 % |
| Flexural modulus | | ASTM D790 | 3100 MPa |
| bending strength | | ASTM D790 | 110 MPa |
| Tensile modulus | | ASTM D638 | 3170 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ASTM D6110 | 304 J/m |
| Impact strength of cantilever beam gap | | ASTM D256A | 21 J/m |
| Dart impact | | 内部方法 | >5.42 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | ASTM D696 | 7.4E-05 cm/cm/°C |
| specific heat | | ASTMC351 | 1460 J/kg/°C |
| thermal conductivity | | 内部方法 | 0.20 W/m/K |
| thermal stability | | ASTM D4802 | Nodegradation |
| Heat distortion temperature | | ASTM D648 | 87.8 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.