Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ASTMD570 | 0.070 % |
| Water absorption rate | | ISO62 | 0.070 % |
| density | | ASTMD792 | 1.02 g/cm³ |
| density | | ISO1183 | 1.02 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 11 g/10min |
| Melt volume flow rate | | ISO1133 | 12.0 cm³/10min |
| Shrinkage rate | | ASTMD955 | 0.65 % |
| Shrinkage rate | | ISO294-4 | 0.30to1.0 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ASTMD2240 | 75 |
| | ISO868 | 65 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | ASTMD542 | 1.573 |
| refractive index | | ISO489 | 1.573 |
| transmissivity | | ASTMD1003 | 91.0 % |
| Haze ratio | | ASTMD1003 | 0.20 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTMD638 | 1640 MPa |
| Tensile modulus | | ISO527-2 | 1550 MPa |
| tensile strength | | ASTMD638 | 25.5 MPa |
| Tensile stress | | ISO527-2 | 27.0 MPa |
| Tensile strain | | ISO527-2 | 2.0 % |
| elongation | Break | ASTMD638 | 220 % |
| Nominal tensile fracture strain | | ISO527-2 | 180 % |
| Flexural modulus | | ASTMD790 | 1330 MPa |
| Flexural modulus | | ISO178 | 1550 MPa |
| bending strength | | ASTMD790 | 27.2 MPa |
| Bending stress | | | 31.0 MPa |
| Bending stress | | ISO178 | 31.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179 | 3.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179 | NoBreak |
| Impact strength of cantilever beam gap | | ASTMD256 | 32 J/m |
| Impact strength of cantilever beam gap | | ISO180/A | 2.0 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/A | 3.0 kJ/m² |
| InstrumentedDartImpact | | ASTMD3763 | 20.1 J |
| film | Test Condition | Test Method | Test Result |
|---|
| elongation | Break | ISO527-3 | 180 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTMD257 | >1.0E+15 ohms·cm |
| Volume resistivity | | IEC60093 | >1.0E+15 ohms·cm |
| dielectric constant | | ASTMD150 | 2.50 |
| dielectric constant | | IEC60250 | 2.50 |
| Dissipation Factor | | IEC60250 | 3E-04 |
| Dissipation Factor | | IEC60250 | 8E-04 |
| CTI | | IEC60112 | 600 V |
| Surface Resistivity | | ASTMD257 | >1.0E+14 ohms |
| Surface Resistivity | | IEC60093 | 1E+15 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 75.6 °C |
| | ISO75-2/B | 75.0 °C |
| | ASTMD648 | 60.0 °C |
| | ISO75-2/A | 58.0 °C |
| vicat | | ASTMD15253 | 87.8 °C |
| vicat | | ISO306/A50 | 81.0 °C |
| vicat | | ISO306/B50 | 51.0 °C |
| | ASTMD696 | 1.3E-04 cm/cm/°C |
| | ISO11359-2 | 6.0E-5to9.0E-5 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare