Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 294-4 | 0.80 % |
| Shrinkage rate | | ISO 294-4 | 0.30 % |
| Water absorption rate | | ISO 62 | 0.60 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94, IEC 60695-11-10, -20 | V-0 |
| UL flame retardant rating | | UL 94, IEC 60695-11-10, -20 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 10200 Mpa |
| Tensile stress | | ISO 527-2 | 170 Mpa |
| Tensile strain | | ISO 527-2 | 2.6 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 50 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 50 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 60 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 62631-3-2 | -- ohms |
| Volume resistivity | | IEC 62631-3-1 | > 1.0E+13 ohms·m |
| dielectric strength | | IEC 60243-1 | 24 KV/mm |
| CTI | | IEC 60112 | 275 V |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 80 °C |
| Drying time - hot air dryer | | | 2.0 到 4.0 hr |
| Suggested maximum moisture content | | | 0.20 % |
| Processing (melt) temperature | | | 280 到 300 °C |
| Melt Temperature, Optimum | | | 290 °C |
| Temperature | | | 70 到 120 °C |
| Mold Temperature, Optimum | | | 100 °C |
| pressure holding | | | 50.0 到 100 Mpa |
| pressure holding | | | yes |
| Hold Pressure Time | | | 3.00 s/mm |
| Maximum Screw Tangential Speed | | | 12 m/min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO 75-2/A | 240 °C |
| Melting temperature 3 | | ISO 11357-3 | 262 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare