PP EPR30R

Properties:
Polymer category
impact resistant multiphase copolymerization
Compare

Technical Data Sheet

Basic performance	Test Condition	Test Method	Test Result
melt mass-flow rate			优等｜1.0-2.0 g/10min
	melt mass-flow rate			一等｜1.0-3.0 g/10min
	melt mass-flow rate	melt mass-flow rate			合格｜0.9-3.1 g/10min

Other performance	Test Condition	Test Method	Test Result
			优等｜≤55 ppm
				一等｜- ppm
					合格｜- ppm
yellow index			优等｜≤4 ppm
	yellow index			一等｜- ppm
	yellow index	yellow index			合格｜- ppm
titanium content			一等｜- ppm
titanium content	titanium content			合格｜- ppm
Total ash content			优等｜≤200 ppm
	Total ash content			一等｜≤300 ppm
	Total ash content	Total ash content			合格｜≤500 ppm
titanium content			优等｜≤3 ppm

Mechanical properties	Test Condition	Test Method	Test Result
tensile yield strength			一等｜21.6 MPa
tensile yield strength	tensile yield strength			合格｜20.5 MPa
Rockwell hardness			优等｜80 R
	Rockwell hardness			一等｜- R
	Rockwell hardness	Rockwell hardness			合格｜- R
Cantilever beam impact strength (V-notch)			优等｜44.1 j/m
	Cantilever beam impact strength (V-notch)			一等｜- j/m
		Cantilever beam impact strength (V-notch)			合格｜- j/m
			Cantilever beam impact strength (V-notch)			优等｜29.4 j/m
				Cantilever beam impact strength (V-notch)			一等｜19.6 j/m
				Cantilever beam impact strength (V-notch)	Cantilever beam impact strength (V-notch)			合格｜15.7 j/m
flexural modulus			优等｜1.029 Gpa
	flexural modulus			一等｜- Gpa
	flexural modulus	flexural modulus			合格｜- Gpa
tensile yield strength			优等｜24.5 MPa

Thermal performance	Test Condition	Test Method	Test Result
			一等｜- ℃
				合格｜- ℃
vicat			优等｜150 ℃
	vicat			一等｜- ℃
	vicat	vicat			合格｜- ℃
			优等｜78 ℃

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.