PP 2C11120 4Plas

Properties:

Filler talc filler 20% filler by weight

Product Description

Certificates(0)

Datasheet

Product Description

Properties:

Filler | talc filler | 20% | filler by weight

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C	ISO 180/1A	4.0	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Hot filament ignition temperature	2.00 mm	IEC 60695-2-13	650	°C
UL flame retardant rating	1.6mm	UL 94	HB
Hot filament ignition temperature	2.0mm	IEC 60695-2-13	650	°C
UL flame retardant rating	1.60 mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	23°C	ISO 527-2/5	2000	MPa
Bending modulus	23°C	ISO 178	2600	MPa
Tensile modulus	23°C	ISO 527-2/5	2000	MPa
tensile strength	Break, 23°C	ISO 527-2/5	23.0	MPa
Tensile strain	Break, 23°C	ISO 527-2/5	14	%
Bending modulus	23°C	ISO 178	2600	MPa
Impact strength of cantilever beam gap	23°C	ISO 180/1A	4	kJ/m²
tensile strength	Break,23°C	ISO 527-2/5	23.0	MPa
Tensile strain	Break,23°C	ISO 527-2/5	14	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	115	°C
Melting temperature		ISO 11357	165	°C
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	115	°C
Melting temperature		ISO 11357	165	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.04	g/cm³
melt mass-flow rate	230°C/2.16kg	ISO 1133	12	g/10min
density		ISO 1183	1.04	g/cm³
melt mass-flow rate	230°C/2.16 kg	ISO 1133	12	g/10 min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.