Technical Data Sheet
| Charpy Notched Impact Strength | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | 可燃性，UL 阻燃等级 | UL 94 | V-0 0.790 mm |
| Thermal performance | 热变形温度，1.8 MPa, 未退火 | ISO 75-2/A | 240 ℃ |
| thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO 75-2/A | 240 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | 0.8mm | UL 94 | V-0 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | Break | ISO 527-2/1A/5 | 1.2 % |
| flexural modulus | 23℃ | ISO 178 | 10500 MPa |
| bending strength | 23℃ | ISO 178 | 150 MPa |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 7.0 kJ/m2 |
| Charpy Notched Impact Strength | 简支梁缺口冲击强度，23℃ | ISO 179/1eU | 20 kJ/m2 |
| density | | ISO 1183 | 1.65 g/cm³ |
| density | | ISO 1183 | 1.65 g/cm3 |
| tensile modulus | | ISO 527-2/1A/1 | 10000 MPa |
| tensile strength | Break | ISO 527-2/1A/5 | 100 MPa |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile modulus | | ISO 527-2/1A/1 | 10000 MPa |
| tensile strength | Break | ISO 527-2/1A/5 | 100 MPa |
| Tensile strain | Break | ISO 527-2/1A/5 | 1.2 % |
| flexural modulus | 23°C | ISO 178 | 10500 MPa |
| bending strength | 23°C | ISO 178 | 150 MPa |
| impact performance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 7.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 20 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.