optical performance	Test Condition	Test Method	Test Result
gloss	45°	ASTM D2457	30

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	-30°C,6.40mm	ASTM D256	120 J/m
	Impact strength of cantilever beam gap	-30°C,3.20mm	ASTM D256	110 J/m
		Impact strength of cantilever beam gap	23°C,6.40mm	ASTM D256	230 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	250 J/m

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus	3.20mm	ASTM D790	1920 MPa
elongation	Break,3.20mm	ASTM D638	40 %
tensile strength	Yield,3.20mm	ASTM D638	37.3 MPa
Tensile modulus	3.20mm	ASTM D638	2380 MPa
bending strength	3.20mm	ASTM D790	60.8 MPa

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature		ASTM D15255	95.0 °C
Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	90.0 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	97.0 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD：3.20mm	ASTM D955	0.40to0.70 %
melt mass-flow rate	220°C/10.0kg	ASTM D1238	4.0 g/10min
density		ASTM D792	1.04 g/cm³

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	96

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.