Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTMD1238 | 1.0到8.0 g/10min |
| Shrinkage rate | | ASTMD955 | 0.20到0.50 % |
| density | | ASTMD792 | 1.20 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTMD785 | 106 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| UL flame retardant rating | | UL94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 53 J/m |
| Impact strength of cantilever beam gap | | ASTMD256 | 80 J/m |
| Impact strength of cantilever beam gap | | ISO180/1A | 6.3 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1 | 6.3 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTMD638 | 93.1 MPa |
| tensile strength | | ASTMD638 | 93.1 MPa |
| elongation | | ASTMD638 | 3.0 % |
| Flexural modulus | | ASTMD790 | 5170 MPa |
| bending strength | | ASTMD790 | 138 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTMD257 | 1E+16 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| RTI Elec | | UL746 | 65.0 °C |
| RTI Imp | | UL746 | 65.0 °C |
| RTI Imp | | UL746 | 65.0 °C |
| RTI | | UL746 | 65.0 °C |
| RTI | | UL746 | 65.0 °C |
| | ASTMD648 | 138 °C |
| | ASTMD648 | 132 °C |
| vicat | | ASTMD15251 | 143 °C |
| RTI Elec | | UL746 | 65.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.