| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.35到1.45 g/cm³ |
| Apparent density | | ISO60 | 0.55到0.70 g/cm³ |
| Shrinkage rate | | ISO2577 | 0.60到0.80 % |
| Water absorption rate | | ISO62 | <1.5 % |
| PostShrinkage | | ISO2577 | 0.40到0.60 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Burning wire flammability index | | IEC60695-2-12 | 900 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 900 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| compression stress | | ISO604 | 200到250 MPa |
| Tensile modulus | Compression Molded | ISO527-2 | 3000到5000 MPa |
| Tensile modulus | Injection | ISO527-2 | 4000到6000 MPa |
| Tensile stress | | ISO527-2 | 50.0到70.0 MPa |
| Tensile stress | | ISO527-2 | 50.0到70.0 MPa |
| Flexural modulus | Compression Molded | ISO178 | 6000到8000 MPa |
| Flexural modulus | Injection | ISO178 | 6000到8000 MPa |
| Bending stress | Compression Molded | ISO178 | 70.0到90.0 MPa |
| Bending stress | Injection | ISO178 | 90.0到110 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | Compression Molded | ISO179/1eA | 1.5到3.5 kJ/m² |
| Charpy Notched Impact Strength | Injection | ISO179/1eA | 2.0到4.0 kJ/m² |
| Impact strength of simply supported beam without notch | Compression Molded | ISO179/1eU | 4.0到6.0 kJ/m² |
| Impact strength of simply supported beam without notch | Injection | ISO179/1eU | 6.0到9.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Dissipation Factor | | IEC60250 | 0.060到0.080 |
| arc resistance | | ASTMD495 | PLC6 |
| CTI | | IEC60112 | >175 V |
| Surface Resistivity | | IEC60093 | 1.0E+13到1.0E+14 ohms |
| Volume resistivity | | IEC60093 | 1.0E+16到1.0E+17 ohms·cm |
| dielectric strength | | IEC60243-1 | 20到30 kV/mm |
| | IEC60250 | 16.012.0 |
| | IEC60250 | 6.004.00 |
| Dissipation Factor | | IEC60250 | 0.60到0.80 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO11359-2 | 2.5E-5到3.5E-5 cm/cm/°C |
| thermal conductivity | | ASTME1461 | 0.20到0.40 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.