Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.42 g/cm³ |
| Humidity Karl Fischer | | ISO15512 | 0.10 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO2039-1 | 196 MPa |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| TristimulusValue | | ISO13468 | 1.7 % |
| TristimulusValue | | DIN5033 | 0.0 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 9400 MPa |
| Tensile stress | Break | ISO527-2 | 122 MPa |
| Tensile stress | | ISO527-2 | 123 MPa |
| Tensile strain | Break | ISO527-2 | 2.0 % |
| Flexural modulus | | ISO178 | 8700 MPa |
| Bending stress | | ISO178 | 185 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 4.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 39 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 36 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 37 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 6.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | 4.0 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 205 °C |
| vicat | | ISO306/B50 | 200 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.