Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO294-4 | 1.3到1.6 % |
| Shrinkage rate | | ISO294-4 | 1.3到1.6 % |
| density | | ISO1183 | 1.13 g/cm³ |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Mold Shrinkage Pressure | | ISO294-4 | 60.0 MPa |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2 | 2500 MPa |
| Tensile stress | | ISO527-2 | 20.0 MPa |
| Tensile strain | | ISO527-2 | 8.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 10 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 100 kJ/m² |
| Impact strength of cantilever beam gap | | ASTMD256A | 50 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| CTI | | IEC60112 | 400 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Continuous use temperature | | | 110 °C |
| vicat | | ISO306/B50 | 80.0 °C |
| Linear thermal expansion coefficient | | ASTMD696 | 5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.