'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PC EXL1132-WH9G700 SABIC INNOVATIVE NANSHA
43
Form：Granules | Grade：Injection grade
Properties:
Low temperature resistancEasy to processHigh mobilityUV resistance
Typical Applications:
Household appliancesAutomotive sectorElectronic fieldElectrical field
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | Household appliances | Automotive sector | Electronic field | Electrical field |
| Properties: | Low temperature resistanc | Easy to process | High mobility | UV resistance |
Certificates
No Data...
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 69.6 | J |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | NoBreak | |
| -30°C | ISO 180/1U | NoBreak | ||
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 55 | kJ/m² |
| -30°C | ISO 180/1A | 20 | kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak | |
| -30°C | ISO 179/1eU | NoBreak | ||
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 60 | kJ/m² |
| -30°C | ISO 179/1eA | 25 | kJ/m² | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| Extreme Oxygen Index | ISO 4589-2 | 32 | % | |
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 875 | °C |
| 1.0mm | IEC 60695-2-13 | 875 | °C | |
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 960 | °C |
| 1.0mm | IEC 60695-2-12 | 850 | °C | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Tensile modulus | ASTM D638 | 2280 | Mpa | |
| ISO 527-2/1 | 2150 | Mpa | ||
| tensile strength | Yield | ASTM D638 | 58.1 | Mpa |
| Yield | ISO 527-2/50 | 57.0 | Mpa | |
| Break | ASTM D638 | 58.7 | Mpa | |
| Break | ISO 527-2/50 | 55.0 | Mpa | |
| elongation | Yield | ASTM D638 | 5.8 | % |
| Tensile strain | Yield | ISO 527-2/50 | 5.0 | % |
| elongation | Break | ASTM D638 | 110 | % |
| Tensile strain | Break | ISO 527-2/50 | 100 | % |
| Bending modulus | 50.0mmSpan | ASTM D790 | 2320 | Mpa |
| ISO 178 | 2240 | Mpa | ||
| bending strength | ISO 178 | 85.0 | Mpa | |
| Yield,50.0mmSpan | ASTM D790 | 95.1 | Mpa | |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Hot deformation temperature | 0.45MPa,Annealed | ISO 75-2/Be | 136 | °C |
| 0.45MPa,Unannealed,3.20mm | ASTM D648 | 137 | °C | |
| RTI Str | UL 746 | 125 | °C | |
| Linear coefficient of thermal expansion | TD：-40to40°C | ASTME831 | 7.6E-05 | cm/cm/°C |
| MD：23to80°C | ISO 11359-2 | 7.5E-05 | cm/cm/°C | |
| MD：-40to40°C | ASTME831 | 7.2E-05 | cm/cm/°C | |
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTM D648 | 124 | °C |
| 1.8MPa,Unannealed,100mmSpan | ISO 75-2/Ae | 125 | °C | |
| Vicat softening temperature | ASTM D152511 | 144 | °C | |
| -- | ISO 306/B50 | 144 | °C | |
| -- | ISO 306/B120 | 145 | °C | |
| Ball Pressure Test | 125°C | IEC 60695-10-2 | Pass | |
| RTI Imp | UL 746 | 120 | °C | |
| RTI Elec | UL 746 | 130 | °C | |
| Linear coefficient of thermal expansion | TD：23to80°C | ISO 11359-2 | 7.5E-05 | cm/cm/°C |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 17 | g/10min |
| Melt Volume Flow Rate (MVR) | 300°C/1.2kg | ISO 1133 | 16.0 | cm3/10min |
| Shrinkage rate | MD：3.20mm | Internal Method | 0.40-0.80 | % |
| TD：3.20mm | Internal Method | 0.40-0.80 | % | |
| Water absorption rate | Saturation,23°C | ISO 62 | 0.35 | % |
| Equilibrium,23°C,50%RH | ISO 62 | 0.15 | % | |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Ball Pressure Test | H358/30 | ISO 2039-1 | 95.0 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.