physical property	Test Condition	Test Method	Test Result	Unit
Melt Volume-Flow Rate (MVR)	220°C/10.0kg	ISO1133	90.0	cm3/10min
Shrinkage rate	MD：23°C	ISO294-4	0.60到0.80	%
Melt Volume-Flow Rate (MVR)	220℃/2.16 kg	ISO 1133	90.0	cm3/10min
Shrinkage rate	MD，23℃	ISO 294-4	0.60 到 0.80	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	23℃	ISO 2039-2	104	R 计秤
Tensile modulus	23℃	ISO 527-2	2280	Mpa
tensile strength	23℃	ISO 527-2	43.0	Mpa
Bending modulus	23℃	ISO 178	2550	Mpa
bending strength	23℃	ISO 178	68.0	Mpa
Impact strength of simply supported beam gap	-30℃	ISO 179	2.0	kJ/m²
Rockwell hardness	R计秤,23°C	ISO2039-2	104
Tensile modulus	23°C	ISO527-2	2280	Mpa
tensile strength	23°C	ISO527-2	43.0	Mpa
Bending modulus	23°C	ISO178	2550	Mpa
bending strength	23°C	ISO178	68.0	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	1.8MPa,未退火	ISO75-2/Af	72.0	°C
Linear coefficient of thermal expansion	MD	ISO11359-2	8E-05	cm/cm/°C
Hot deformation temperature	1.80MPa，未退火	ISO 75-2/Af	72.0	°C
Linear expansion coefficient	流动	ISO 11359-2	0.000080	cm/cm/℃
Flame retardant grade	0.800mm	UL 94	V-2

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.8mm	UL94	V-2
UL flame retardant rating	UL flame retardant rating	3.0mm	UL94	V-2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.